Analysis of Bending Strength of Resin Mortars That Are at Risk of Long-Term Exposure to Environmental Corrosives

World Multidisciplinary Earth Sciences Symposium 2017

Debska, Bernardeta^1 ; Licholai, Lech^1

Department of Building Engineering Rzeszow, University of Technology, ul. Poznaska 2, Rzeszów

35-959, Poland^1

关键词: Aggressive medium;    Environmental problems;    Long term exposure;    New building materials;    Poly (ethylene terephthalate) waste;    Propylene glycols;    Strength parameters;    Strength property;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/95/4/042015/pdf
DOI  :  10.1088/1755-1315/95/4/042015

来源: IOP

【 摘 要 】

The results of the article are part of an extensive research on new building materials including cement-free polymer composites where the binder is epoxy resin modified with glycolyzates obtained from poly (ethylene terephthalate) waste (PET). The investigation conducted con-firmed that there is a possibility of using waste materials in the production of mortar. Since they have always been an environmental problem, their utilization will help to apply the principles of sustainable development in the processes of obtaining new materials. The article discusses the results of a study of flexural strength of polymer mortars. Mortar specimens modified with propylene glycol and PET waste based glycolyzate were exposed to a 10% NaCl solution and their strength parameters were then examined after one month, six months and twelve months of immersion in this aggressive medium. The same characteristics were also determined for specimens that were not exposed to the NaCl solution. The results were presented as the trend function. The sections of the curve corresponding to the particular periods of exposure in aggressive medium vary in shape. Due to this, an attempt was made to adjust the spline function to the experimental data. The composites obtained show a deterioration in their strength properties which grows with the extension of their exposure to a corrosive medium. However, the chemical corrosion resistance of the mortars under investigation can be considered very good as it is still much higher than that of conventional cement mortars. Even after a year exposure to a corrosive substance, the mortars obtained still show high mean flexural strength values which equal about 30 MPa.