An attempt to apply a slag binder with zeolite in mining construction. Durability and hardness | |
生态环境科学 | |
Slomka-Slupik, B.^1 ; Podwórny, J.^2 ; Polus, M.^3 | |
Silesian University of Technology, Faculty of Civil Engineering, 5 Akademicka Street, Gliwice | |
44-100, Poland^1 | |
Institute of Ceramics and Building Materials, Refactory Materials Division, 99 Toszecka Street, Gliwice | |
44-100, Poland^2 | |
P.P.U.W. ANKRA Marian Polus, 5 Zabiniec Street, Kraków | |
31-215, Poland^3 | |
关键词: Compression strength; Ground granulated blast-furnace slag (GGBFS); Microscopic observations; Microstructure observation; Mining constructions; Rheological property; Steel reinforcements; Vickers indenters; | |
Others : https://iopscience.iop.org/article/10.1088/1755-1315/261/1/012046/pdf DOI : 10.1088/1755-1315/261/1/012046 |
|
学科分类:环境科学(综合) | |
来源: IOP | |
【 摘 要 】
The paper presents comparative results of strength tests on mortars, hardness of pastes and their microscopic observations. The focus was on alkali activated ground granulated blast furnace slag (GGBFS) to which the zeolite was introduced. Zeolite positively affects the rheological properties, densifies the microstructure by reducing its permeability and binds Ca(OH)2. It causes lower susceptibility of the binder to corrosion, which can be affected by mine mineralized waters or brines flowing from the salt beds. To increase the mechanical properties, polymer scattered reinforcement was used, which does not corrode in contact with saline waters, contrary to steel reinforcement. The paper presents the results of: Bending strength and compression strength of mortar bars made of slag (S2), slag with zeolite (S3), slag with zeolite and polymer fibers (S5); the Vickers indenter tests results of slag pastes of S2 and S3 as well, up to 90 days of hydration. The 90 day compressive strength was 64.0 MPa; 27.7 MPa and 64.7 MPa, and bending strength: 6.4 MPa; 2.9 MPa and 6.0 MPa, respectively for S2, S3, S5. The Vickers indenter test at HV 1 was as follows: On average 27.04 MPa and 36.69 MPa, respectively for S2 and S3. Microstructure observations were carried out in SEM. The obtained results require further research work.【 预 览 】