Effect of Process Parameters on Structure and Mechanical Properties of Friction Stir Welding Joint of 5052 Aluminum Alloy
Zhou, Zejie^1 ; Huang, Zhichao^1
Key Laboratory of Conveyance and Equipment, Ministry of Education, School of Materials Science and Engineering, East China Jiaotong University, No.808 Shuanggang East Street, Nanchang, Jiangxi
330013, China^1
关键词: 5052 aluminum alloy;    Friction stir welding joints;    Microstructure and mechanical properties;    Process parameters;    Rotational speed;    Static strength;    Tensile fractures;    Welding process;   
Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/585/1/012009/pdf
DOI  :  10.1088/1757-899X/585/1/012009
来源: IOP
PDF
【 摘 要 】

2.5 mm thick sheets of AA5052 were welded using friction stir welding technology. The effects of welding speed, rotational speed of pin, length of pin, single-side and double-side welding process on the morphology, microstructure and mechanical properties of welded joints were studied and analyzed. The failure mode was studied. The results show that the joints with good mechanical properties and without welding defects can be welded when the rotational speed of pin is 500-1200r/min and the welding speed is 100-480mm/min. The microstructure of weld nugget is mainly composed of α phase solid solution and β phase particles. The process parameters of friction stir welding have great influence on the static strength of welded joints. The static strength increases with the increasing of rotational speed of pin, however decreases with the increasing of welding speed. The peak load of the double-side welding increases by 30% compared with the single-side welding. The length of pin has little effect on the tensile strength. The tensile fracture of the single-side welding is located in the weld nugget zone, whereas the fracture of double-side welding is located in the base material zone.