Preparation and Properties of SiC Porous Ceramics with Double-Particle Size | |
Xu, Chengshi^1 ; Dong, Youming^1 ; Liu, Yang^1 ; Li, Huan^1 ; Deng, Xiangyun^1 | |
College of Physics and Materials Science, Tianjin Normal University, Tianjin | |
300387, China^1 | |
关键词: Filtration pressures; Pore making agents; Pore-forming agents; Porous ceramics; SiC particles; Single particle; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/585/1/012001/pdf DOI : 10.1088/1757-899X/585/1/012001 |
|
来源: IOP | |
【 摘 要 】
In this paper mixed two kinds of SiC particles with different diameter (50-70 mesh and 80-90 mesh) as aggregate of SiC porous ceramics. And the porous ceramic properties were measured when the pore-making agent was 7.5wt%, 10wt% and 15wt% respectively. The experiments show that the porosity, flexural strength and filtration pressure drop of double-particle size porous ceramics is optimized compared with single size porous ceramics. In the pore-forming agent was 10wt% and 50-70 mesh SiC particle was 10wt%, the flexural strength was 40.71MPa, and porosity was 35.69%. It was 4.76MPa and 6.9% higher than single-particle size sample, and the filtration pressure drop has a significant decrease.【 预 览 】