Comparative Analysis of Different Surface Modification Processes on AA 7075 T651

International conference on Materials Engineering and characterization

工业技术（总论）;材料科学

Abeens, M.^1 ; Muruganandhan, R.^1 ; Thirumavalavan, K.^1

AU FRG Institute for CAD/CAM, Department of Mechanical Engineering, Anna University, Tamil Nadu, Chennai

600025, India^1

关键词: Comparative analysis;    Deformed layers;    High-strength materials;    Laser shock peening;    Mechanical treatments;    Surface hardness;    Surface modification process;    Vickers microhardness;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/574/1/012018/pdf
DOI  :  10.1088/1757-899X/574/1/012018

来源: IOP

【 摘 要 】

Modern industries turn into light weight high strength materials. Aluminum alloys are having such a great property, in which, AA 7075 T651 provides good strength than other alloys. Hence, hardness of aluminum alloys are poor there by improvement of surface hardness of aluminum alloy is necessitate. Shot peening, severe surface mechanical treatment (SSMT) and laser shock peening (LSP) are the surface property enhancement processes, which are used to improve the surface hardness of AA 7075 T651. This article deals with study the effect of shot peening, Severe surface modification process and laser shock peening on AA 7075 T 651. Among these two processes, LSP reveals better improvement in surface hardness. The Vickers micro hardness test is contacted on the specimens. 15%, 18% and 29% of harness improvements are obtain than unpeened specimen in shot peened specimen, SSMT specimen and Laser shock peened specimen respectively. The deformed layer thickness is 500 μm found in the laser shock peened specimen and 300 μm in the shot peened and SSMT treated specimens.