Morphology and phase composition of hybrid powders based on aluminum, synthesized for a gas-dynamic spraying of coatings by milling

International Conference on Synthesis and Consolidation of Powder Materials

Sobol'Kov, A.V.^1 ; Aborkin, A.V.^1

Vladimir State University Named after Alexander and Nikolay Stoletovs, Vladimir, Russia^1

关键词: Al2O3 particles;    Average particle size;    Cold gas dynamic spraying;    Functional coating;    Matrix materials;    Mechanical processing;    Planetary ball mill;    Synthesized powder;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/558/1/012049/pdf
DOI  :  10.1088/1757-899X/558/1/012049

来源: IOP

【 摘 要 】

Hybrid powders of the AlMg2 + 1 wt % TiC/MWNT + 10-50 wt % Al2O3 system were obtained using the method of mechanical processing in a planetary ball mill. The powders were characterized using the methods of scanning electron microscopy, particle size distribution testing and X-ray analysis. It is shown that an increase in the content of Al2O3 particles from 10 to 50 wt % leads to a decrease in the average particle size of the synthesized powder from 49 to 16 μm, respectively. The proportion of particles smaller than 5 μm, depending on the concentration of Al2O3, varies in the range of 1.2-15.1%. At the same time, the size of the matrix material crystallites decreases from 58 and 52 nm, respectively. The resulting hybrid powder can be used to create functional coatings using cold gas-dynamic spraying.