Effect of Titanium Dioxide Particle Size in Water-based Micro/Nanofluid as Quench Medium in Heat Treatment Process
材料科学;金属学
Prayogo, I.F.^1 ; Muhammad, F.^1 ; Rakhman, D.^1 ; Putra, W.N.^1 ; Harjanto, S.^1
Department of Metallurgy and Materials Engineering, Faculty of Engineering, Universitas Indonesia, Depok, Indonesia^1
关键词: Cooling characteristics;    Energy dispersive spectroscopies (EDS);    Heat treatment process;    Micro-size particles;    Nano-sized particles;    Nanofluids;    TiO2;    Titanium dioxide particles;   
Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/547/1/012064/pdf
DOI  :  10.1088/1757-899X/547/1/012064
学科分类:材料科学(综合)
来源: IOP
PDF
【 摘 要 】

Recently, nanofluid is used to improve the thermal conductivity of the quench medium in the heat treatment industry. In this research, ball-milled micro-sized TiO2 powder and nano-sized TiO2 particle were used and compared for their cooling characteristic in a micro/nanofluid. The micro/nanofluids were produced by mixing 0.1%, 0.3%, and 0.5% volume of both micro- A nd nano-sized particle into 100 ml of distilled water. The planetary ball mill was used at 500 rpm for 15 hours to reduce the dimension of micron-sized TiO2. Composition characterization by Energy Dispersive Spectroscopy (EDS) showed that the powder used were free from impurities. Nanofluids were then used to quench S45C carbon steel samples, which heated at 1000°C for 1 hour. The hardness test result showed that the sample quenched with 0.5%addition of the nano-sized particle in nanofluid had the highest number up to 691 HV, almost 100HV increment from a water-quenched sample where the hardness was 598 HV, showing that the cooling rate in the nanofluid was much higher. The addition of micro-size particle in fluid generally had a lower cooling rate than the addition of nano-size particle.