Investigation of corrosion rate on the modified 410 martensitic stainless steel in tempered condition

International Seminar on Metallurgy and Materials

Prifiharni, S.^1 ; Sugandi, M.T.^2 ; Pasaribu, R.R.^2 ; Sunardi^2 ; Mabruri, E.^1

Research Center of Metallurgy and Material, Indonesia Institute of Science Building 470, Puspiptek Area, Tangerang Selatan, Banten

15314, Indonesia^1

Departement of Mechanical Engineering, Engineering Faculty University of Sultan Ageng Tirtayasa, Jl. Jend. Sudirman Km.3, Cilegon - Banten

42435, Indonesia^2

关键词: Concentration of solutions;    Corrosion tests;    Increasing temperatures;    NaCl concentration;    NaCl solution;    Oil quenching;    Tempering temperature;    Turbine blade;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/541/1/012001/pdf
DOI  :  10.1088/1757-899X/541/1/012001

来源: IOP

【 摘 要 】

Martensitic stainless steels were usually used for turbine blade. Their properties can be improved in various ways, such as by heat treatment. This paper reports the influences of tempering temperature and holding time in various concentration and temperature of NaCl solution on corrosion rate of the modified 13Cr martensitic stainless steels. Samples were austenized at 1050°C for 1 hour followed by oil quenching. The austenized sample were tempered at 600°C, 650°C, and 700°C for 1, 3, and 6 hours. All tempered specimens were immersed in 20% NaCl concentration for 120 hours and tempered specimen at 700°C for 6h was prepared for another corrosion test. Samples were immersed in different concentration of NaCl solution 3.5%; 10%; and 20% at room temperature, 60°C, and 80°C. Increasing temperature and concentration of solution will lead to corrosion rate increased. However, corrosion rate slightly decreases at higher temperature due to dissolved oxygen was decreased.