International Scientific and Technical Youth Conference "Perspective Materials of Constructional and Medical Purpose" | |
Alumina-based composites reinforced with single-walled carbon nanotubes | |
材料科学;医药卫生 | |
Leonov, A.A.^1 ; Abdulmenova, E.V.^1 | |
National Research Tomsk Polytechnic University, 30 Lenin Ave., Tomsk | |
634050, Russia^1 | |
关键词: Al2O3 ceramics; Alumina-based composites; Average values; Composite powders; Particle rearrangement; Single-walled carbon nanotube (SWCNTs); Sintering behaviors; Sintering temperatures; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/511/1/012001/pdf DOI : 10.1088/1757-899X/511/1/012001 |
|
来源: IOP | |
【 摘 要 】
Monolithic Al2O3 ceramics and Al2O3-3 vol% single-walled carbon nanotubes (SWCNTs) composites were prepared by spark plasma sintering. The influence of SWCNTs and sintering temperature on sintering behavior and mechanical properties were investigated. Nanotubes were relatively homogeneously distributed in the composite powder, although some agglomerates/bundles existed. It was found that SWCNTs addition retards slightly the sinterability of alumina by nanotubes hindering of particle rearrangement. The average microhardness of the composites was lower than that of Al2O3 ceramics, but there were also high microhardness values of composites (20.41 GPa). The reduction in microhardness is explained in this paper. The average values of the fracture toughness (4.94 MPa-m1/2) from the composite sintered at 1500 °C were approximately 6% and 12% higher than those from the Al2O3 ceramics sintered at 1500 °C and 1600 °C, respectively. In addition, the analysis of the phase composition and the parameters of the crystal structure of the samples were made.