Nafion? and polyaniline composite modification with Li and Mg ions

Functional Materials and Nanotechnologies 2018

Lozkins, Stanislavs^1^2 ; Hodakovska, Julija^1 ; Kleperis, Janis^1 ; Merijs-Meri, Remo^2

Institute of Solid State Physics, University of Latvia, Latvia^1

Department of Polymer Materials Technology, Riga Technical University, Latvia^2

关键词: Impedance spectroscopy;    Physio-chemical properties;    Polyaniline composites;    Polyaniline emeraldine salts;    Synthesized materials;    Temperature intervals;    Thermal characteristics;    Working temperatures;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/503/1/012031/pdf
DOI  :  10.1088/1757-899X/503/1/012031

来源: IOP

【 摘 要 】

Modification of Nafion®-based samples with polyaniline (PANI) and positive charged ions could potentially allow achieving good proton conductivity at higher working temperatures what is observed in typical polymer electrolyte membrane fuel cells. In this work Nafion® polymer was modified with 1% polyaniline emeraldine salt and Li and Mg ions containing solutions. The influence of activation process and the type of ions on composites' proton conductivity was investigated. To define the best composition the physiochemical properties of synthesized materials were determined by the means of thermogravimetric analysis, impedance spectroscopy, determination of water absorption and its kinetics, and FTIR. From the original samples the best results of σ=155 mS/cm were shown by Nafion®/PANI membrane what was modified by Li+ reduction solution. This membrane also had better thermal characteristic compared to other researched samples: membrane degradation starts on higher temperature interval.