Relationship Between Air-Content in Fresh Cement Paste, Mortar, Mix and Hardened Concrete Acc. to PN-EN 480-1 with Air-Entraining CEM II/B-V

3rd World Multidisciplinary Civil Engineering, Architecture, Urban Planning Symposium

土木建筑工程;文学

Lazniewska-Piekarczyk, Beata^1 ; Golaszewski, Jacek^1

Silesian Technical University, Faculty of Civil Engineering, Department of Building Materials and Processes Engineering, Akademicka 5 Str., Gliwice

44-100, Poland^1

关键词: Air entraining admixtures;    European Standards;    Good correlations;    Hardened concrete;    Porosity structure;    Research results;    Specific surface;    Volumetric methods;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/471/3/032044/pdf
DOI  :  10.1088/1757-899X/471/3/032044

学科分类：土木及结构工程学

来源: IOP

【 摘 要 】

Research results of the relationships between air-volume in air-entrained cement paste, mortar and concrete, all designed according to PN-EN 480-1 guidelines are presented in the paper. The cement paste, mortar and concrete, with w/c=0,5 ratio, were prepared using innovative air-entraining cement CEM II/B-V. The air-entraining cement CEM II/B-V was produced using two methods: mixed together with natural or synthetic aerated admixture. The air volume test of the volumetric method was carried out in case of fresh cement paste, mortar and concrete mix. Fresh concretes were evaluated in terms of stability of air entrainment and consistency for 5, 20 and 40 min. The porosity structure parameters, like summarized air-content, specific surface of air voids, air-voids spacing factor and micropores content of hardened concrete, were estimated using computer tomography with a resolution of 2-5 μm. The aim of the research was to determine the dependence between air-content of cement paste, mortar and concrete on the measurement of air-entrainment of cement paste or mortar with the same w/c ratio and type of cement, all designed according to PN-EN 480-1 guidelines. Test results proved that there is a good correlation between the measured air-content of the cement paste, mortar and concrete. Therefore, it is possible to predict the aeration of concrete on the air-entrainment of the mortar. Moreover, the porosity parameters research results indicated, that the air-entrainment of concrete is very stable. Research results indicated that the porosity of hardened concrete meets the European standards for frost-resistant concrete. Research results of the influence of air- entraining admixture type have proved, that a greater amount of micro pores in concrete is the effect of a synthetic air-entraining admixture. In concrete with synthetic entraining admixtures the air pores have smaller diameters than in concrete with natural air-entraining admixture, which are being transferred into their specific surface. The synthetic admixture is more recommended than the natural one also because of the value of the air-voids spacing factor of concrete.