Effect of fibre-lasers parameters on interfacial reaction and wetting angle of two different types of SAC305 solder fabrication on Cu pad

1st International Postgraduate Conference on Mechanical Engineering

工业技术（总论）;机械制造

Nabila, T.J.^1 ; Idris, S.R.A.^1 ; Ishak, M.^1

Faculty of Mechanical Engineering, Universiti Malaysia Pahang, Pekan, Pahang

26600, Malaysia^1

关键词: Continuous lasers;    Heat distribution;    Intermetallic compound thickness;    Laser soldering;    Metallurgical microscope;    Scanning time;    Solder joints;    Solder powders;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/469/1/012117/pdf
DOI  :  10.1088/1757-899X/469/1/012117

学科分类：工业工程学

来源: IOP

【 摘 要 】

This paper presents the effect of different parameters of fibre laser soldering on interfacial reaction of two types of lead-free solder fabrication on Cu pad. The objective of this paper is to study the intermetallic compound thickness (IMC) formation and wetting angle of two different types of solder fabrication when it was exposed to varies of laser power and scanning time. A fibre laser with 200W continues wave (CW) was used in this experiment to form a joining between SAC305 solder wire and printed copper board. A continuous laser power was ranged between 72W to 88W and scanning time of 1.5s and 2.5s were chosen to create joining. Flux was used in the laser soldering experiment in order to gain uniform heat distribution throughout the solders. The mechanical properties were observed by using optical and metallurgical microscope. Results showed that SAC305 solder powder performing good wetting angle with smallest value of 18.18° meanwhile, the smallest wetting angle for solder wire is 26.12° and in terms of IMC layer comparison, solder powder has more thinner IMC layer with value of 1.1 μm compared to SAC305 solder wire which is 2.9 μm. Thus, it is showed that solder powder improved the solder joint properties compared to conventional solder wire when exposed to laser soldering.